Abration Test

Wear medium： CS-10、H-18

rotate speed：60 or 72 circles per min

Load：250g，500g，1000g  

available revolution： maximum 50000 revolutions

test method：ASTM D3884、ASTM D1175、ASTM D1044、ASTM D4060、TAPPI T476、ISO 9352、ISO 5470-1、JIS K7204、JIS A1453、JIS K6902、JIS L1096、JIS K6964、DIN 52347、DIN 53109、DIN 53754、DIN 53799

TABER 5135

application：

Products used on the test surface, such as suitcases, carpets, cardboard, clothing, glass, plastic coatings, ceramic tiles, metal coatings, paints, varnishes, decorative foils, high-pressure foils, plastics, textiles, flexible floor mats, traffic paints, Anodized layers, blankets, electronic components, decorative panels, waxes, labels, leather covers, dental materials, automotive interiors, resins, furniture, etc.

specialty：

Unique wear process：The material to be tested is placed on a turntable and the two grinding wheels are pressed against the material with a certain weight so that it is worn. The grinding wheel rotates with the rotating surface of the sample disc, causing relative movement and wear, and the deflection of the grinding wheel shaft with respect to the rotating shaft of the rotating disc during the rotation produces a slip movement, thereby abrading the material. Equipped with a vacuum system to absorb wear generated substances When the sample with an area of 10x10cm is subjected to wear, the surface material of the sample is abraded by full-angle particles or filaments to form a complete ring.

Simulation of real use conditions： Different kinds of abrasive media and accessories can be selected for different tests. Repeated tests can be performed at the same point on one material, with a material thickness of approximately 0.5" broken or worn off. Two speeds can be set (60, 72 rpm), 0-50000 rpm (100 can be quickly set , 500, 1000 or 2500 rpm) and 3 kinds of loads.